Effect of Repeated Firings on Color Stability of Zirconia Reinforced Lithium Silicate and Lithium Disilicate Ceramics

Purpose: The purpose of this invitro study was to assess the changes in the color attributes of high-translucency (HT) lithium disilicate and zirconia-reinforced lithium silicate in BL3/0M1, A1, A2, and A3 shades during first, second, and third firing cycles. Materials and Methods: Eighty specimens of two ceramic systems (IPS e.max CAD and Vita Suprinity) in BL3/0M1, A1, A2, and A3 shades, were prepared in thickness of 1 mm (n=10). Each group was subjected to 3 firing cycles and the CIE L*a*b* color parameters of specimens were measured after each firing cycle by a reflectance spectrophotometer. The color change (∆E) between each two firing cycles was calculated by the relevant equation. Data were analyzed by one-way ANOVA and Tamhane post hoc test. Results: All ∆E values were significant (P<0.001) except for ∆E2-1 (color difference between second and first firing) and ∆E3-2 (color difference between third and second firing) in A2 shade of IPS e.max (P=0.436) and ∆E2-1 and ∆E3-2 in 0M1 shade of Suprinity (P=0.345). Conclusion: Repeated firing resulted in generally higher ∆E in ZLS than LDS, and 0M1 Suprinity experienced maximum ∆E after repeating firing.

Lithium Disilicate Zirconium Oxide Computer-Aided Design Color