Effect of Cement Space on the Marginal Adaptation of Monolithic Zirconia Crowns

Abstract

Purpose: To evaluate effect of cement space on marginal fit of monolithic zirconia crowns after sintering, glazing, and cementation. Materials and Methods: Molar typodont teeth were prepared to receive crowns, and were scanned with a laboratory scanner to generate virtual dies. Crown design was planned with the CAD software with a simulated cement space of 60 µm or 80 µm. Zirconia crowns for the 60 µm and 80 µm groups were milled from zirconia discs. Milled crowns were sintered, glazed, and cemented. Marginal discrepancy was measured after sintering, glazing, and cementation. Measurements were carried out under 200X magnification, and data obtained were statistically analyzed. Results: Increasing cement space from 60 to 80 µm resulted in a non-significant decrease in marginal discrepancy. Marginal discrepancy was the lowest in the post sintered specimens, and increased significantly after glazing and cementation in both the groups. Conclusions: It was concluded that the glazing and cementation procedures significantly increased the marginal discrepancy. Increasing the cement space resulted in an insignificant decrease in the marginal discrepancy. Clinical relevance: The results of this study suggest that 60 µm of simulated cement space is recommended for achieving clinically acceptable marginal fit of the monolithic zirconia crowns.

ABSTRACT
Keywords
Marginal Adaptation
Monolithic Zirconia
CAD-CAM
Cement Space

Authors

Rahul S. Kulkarni, Priyanka Singh

Articles from this issue

Title / DOI Access Page Start Page End Purchase
Survival of CAD/CAM Feldspathic Crowns in Brazilian Navy Dentistry: 24 Months of Preliminary Study
10.1922/EJPRD_2810Michelon07
no access 123 129 £10.00
Effect of Cement Space on the Marginal Adaptation of Monolithic Zirconia Crowns
10.1922/EJPRD_2804Singh06
no access 130 135 £10.00
Influence of Thermal Tempering Processes on Color Stability of Glassinfiltrated Monochrome and Multilayer 5 mol% Yttria Partially Stabilized Zirconia
10.1922/EJPRD_2832Uasuwan12
no access 136 147 £10.00
Masking Ability of Prosthetic Substrates by a Conventional Resin Luting Agent and the Effect of the Core on the Final Color of Lithium Disilicate Crowns
10.1922/EJPRD_2790Fehrenbach07
no access 148 154 £10.00
A Novel Artificial Intelligence Approach to Kennedy Classification for Partially Edentulous Patients Using Panoramic Radiographs
10.1922/EJPRD_2801Hassan09
no access 155 163 £10.00
Carbamide and Hydrogen Peroxide Bleaching Effect on Modern CAD/CAM Dental Ceramics: An Investigation on Ion Release and Surface Characteristics
10.1922/EJPRD_2794Vavrickova08
no access 164 171 £10.00
Influence of Different Finish Line Types on the Penetration Properties of Elastomeric Impression Materials
10.1922/EJPRD_2746Pewhom08
no access 172 179 £10.00
Cutting Efficiency of Diamond Burs with Different Coatings on Ceramic and Resin Composite Materials after Multiple Use
10.1922/EJPRD_2892Erlinger09
no access 180 188 £10.00
Adhesive Type, Application Mode and Composite Preheating Influence Temperature Changes Across Different Dentin Thicknesses
10.1922/EJPRD_2823Wahby10
no access 189 198 £10.00
Air Abrasion vs. Tribochemical Silica Coating: Effect on Translucent Zirconia Bond Strength
10.1922/EJPRD_2799Prochnow07
no access 199 205 £10.00
Intraoral Scanning Versus Conventional Impression for Implant Prostheses: A Systematic Review
10.1922/EJPRD_2811Ribeiro13
no access 206 218 £10.00
  • free access Free Access
  • no access No Access
  • full access Full Access

Subscriptions